Alliage 904 L : comportement électrochimique en milieux phosphoriques pollués par les ions sulfures et fluorures en condition de corrosion-abrasion
Corrosion-abrasion of 904 L stainless steel in phosphoric acid media polluted by sulfide and fluoride ions
1 Laboratoire d’Electrochimie-Corrosion, Faculté des Sciences, Université Mohammed V, Rabat (Maroc)
2 Equipe de Métallurgie Physique-Laboratoire des Matériaux (UPRESA-CNRS 5071), Ecole Nationale Supérieure de Chimie (INPT), Toulouse (France)
La corrosion-abrasion de l’acier austénitique 904 L (X1NiCrMoCu 25-20-5) en milieu phosphorique pollué par les ions sulfures et fluorures a été étudiée par des techniques électrochimiques et physiques.
L’étude quantitative de la corrosion-abrasion a montré que la perte de masse totale du matériau résulte essentiellement de l’effet mécanique et de l’action de synergie entre corrosion et abrasion. Dans ces conditions, l’addition des ions sulfures et fluorures dans le milieu électrolytique entraîne une activation de la dissolution et une altération de la passivité (corrosion localisée). Ces effets s’accentuent avec l’accroissement de la teneur du milieu en impuretés.
Les informations obtenues sur le film de passivité par les techniques d’analyse de surface (SIMS et EDS) ont révélé la présence des ions sulfures et fluorures dans le film formé.
Abstract
The corrosion-abrasion of an austenitic alloy 904 L (X1NiCrMoCu 25-20-5) in a phosphoric acid media containing sulfide and fluoride ions has been studied by means of electrochemical and physical methods.
The quantitative study of corrosion-abrasion has shown that the total loss of the material mass results is mainly due to mechanical effect and synergistic action of corrosion and abrasion. In these conditions, the addition of S2– and F– ions to an electrolytic media accelerates the electrochemical processes decreasing resistance of the material. These ions induce the activation of the material and make difficult the passivation (localized attacks).
The informations obtained on the passivity film by surface analysis technics (SIMS and EDS) revealed the presence of sulfide and fluoride in the film formed at the material surface.
© SIRPE 1998
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.