I - Modélisation phénoménologique de la corrosion sous contrainte
Phenomenological modelling of stress corrosion cracking
Abstract
The morphological model provides a method for a quantitative characterization of stress corrosion cracking without any mechanistic hypothesis. It consists in analyzing the morphological information (shape of the cracks and size distribution) present in a specimen after a constant extension rate test. It is shown that this experimental datum can be used for the calculation of initiation and propagation rates. An application of this morphological model is performed using the couple 304L austenitic stainless steel/boiling 44 weight percent MgCl2 aqueous solution. This study provides analytical expressions of the crack initiation and growth rates. The limitations of this modelling are presented and other studies are proposed.
© SIRPE 1995
Les statistiques affichées correspondent au cumul d'une part des vues des résumés de l'article et d'autre part des vues et téléchargements de l'article plein-texte (PDF, Full-HTML, ePub... selon les formats disponibles) sur la platefome Vision4Press.
Les statistiques sont disponibles avec un délai de 48 à 96 heures et sont mises à jour quotidiennement en semaine.
Le chargement des statistiques peut être long.