Deformation behavior of ultra high-purity Fe-50 MASS %Cr alloyed with tungsten

Mécanismes de déformation d’alliages Fe-50pds% Cr ultra purs dopés au tungstène

¹ Nisshin Steel Co. Ltd., Shunan 746-8666, Japan
² Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan

Abstract

The deformation mechanisms and the effect of W on the mechanical properties of high-purity Fe-50mass%Cr alloys were investigated by tensile test between 293 K and 773 K. The deformation of the W-free alloy at 293 K proceeds both by slip and twinning. Serration at 573 K is possibly caused by dynamic strain aging. Twin deformation occurs frequently at 673 K and 773 K. 0. 2% proof stress and tensile strength increase with test temperature between 673 K and 773 K. Hardening is due to age-hardening. Twin deformation is promoted by W atoms in solution in the matrix. The tensile strength increases with W content at every test temperature. The ductility at 673 K and 773 K is improved by W.

Résumé

Les mécanismes de déformation et l’effet de W sur les propriétés mécaniques d’alliages Fe-50pds% Cr de haute pureté ont été étudiés en traction entre 293 K et 773 K. La déformation de l’alliage sans W, à 293 K, s’effectue à la fois par glissement et maclage. Les oscillations à 573 K sont sans doute produites par vieillissement sous contrainte dynamique. La déformation par maclage se produit à 673 et 773 K. La limite d’élasticité conventionnelle à 0, 2 % et la charge de rupture augmentent avec la température entre 673 et 773 K. Le durcissement est produit par le vieillissement. La déformation par maclage est due à la présence de atomes de W en solution. La charge de rupture augmente avec la teneur en W, quelle que soit la température. La ductilité à 673 et 773 K est améliorée par le tungstène.