Matériaux & Techniques
Volume 101, Number 5-6, 2013
Corrosion et protection des ouvrages métalliques en environnement marin / Corrosion and protection of metallic structures in marine environments
|
|
---|---|---|
Article Number | 503 | |
Number of page(s) | 10 | |
DOI | https://doi.org/10.1051/mattech/2013086 | |
Published online | 20 December 2013 |
Effets des ruptures et reprises de protection cathodique sur la couche de produits de corrosion des aciers en zone de marnage
Effects of cathodic protection breakdowns and resumptions on the steel corrosion products layer in the tidal zone
1 Laboratoire des Sciences de
l’Ingénieur pour l’Environnement (LaSIE), FRE 3474 CNRS, Université de La Rochelle,
Bât. Marie Curie, Av. Michel
Crépeau, 17042
La Rochelle Cedex 01,
France
prefait@univ-lr.fr; rsabot@univ-lr.fr; mjeannin@univ-lr.fr
2 Corrodys, 145 chemin de la
Crespinière, BP 48, 50130
Cherbourg-Octeville,
France
hantony@corrodys.com
3 Accoast SAS, Espace Atlantis, 7 Parc
d’Activité Doaren Molac, 56610
Arradon,
France
samuel.pineau@accoast.fr
Reçu :
4
Juillet
2013
Accepté :
29
Novembre
2013
Des coupons en acier au carbone ont été exposés en zone de marnage dans deux sites portuaires (Le Havre et Nantes-Saint Nazaire) pendant 7 ans en étant soumis à une protection cathodique permanente, à une protection limitée aux 6 premières années ou à une protection appliquée seulement la dernière année. La couche de produits recouvrant les coupons a été analysée en détail par diffraction des rayons X et μ-spectroscopie Raman et les vitesses de corrosion ont été estimées par des mesures de perte d’épaisseur. Les coupons ayant été protégés en permanence se caractérisent par des vitesses de corrosion environ 10 fois plus faibles que celles observées en l’absence de protection. Les produits de la corrosion résiduelle sous protection cathodique, similaires à ceux observés en corrosion libre, forment une fine couche au contact du métal sous le dépôt calcomagnésien. L’arrêt de la protection au bout de 6 ans conduit à une ré-accélération de la dégradation qui se traduit par l’accumulation rapide des produits de la corrosion libre. Ceci confirme que la protection cathodique a essentiellement un effet modérateur sur la cinétique d’un processus qui reste globalement le même. Enfin, l’application différée de la protection après 6 ans induit la transformation de certains constituants de la rouille, notamment celle de la rouille verte sulfatée en rouille verte carbonatée. D’autres constituants prédominants, comme la magnétite, ne sont pas affectés. La couche de rouille pré-existante subit donc des modifications plus ou moins importantes selon sa composition.
Abstract
Carbon steel coupons were set in the tidal zone of two seaports (Le Havre and Nantes-Saint Nazaire) for 7 years with a cathodic protection applied permanently, stopped after 6 years or applied only the last year. The products covering the coupons were thoroughly characterized by X-ray diffraction and μ-Raman spectroscopy, and the corrosion rates were estimated by residual thickness measurements. Permanently protected steel coupons are characterized by corrosion rates ten times smaller than those measured for unprotected coupons. The products of the residual corrosion process, similar to those observed at the open circuit potential, form a thin layer on the steel surface under the calcareous deposit. Stopping cathodic protection after 6 years induces a re-acceleration of the degradation, as revealed by the accumulation of the usual corrosion products. This confirms that cathodic protection has mainly a moderating effect on the kinetics of a process basically unchanged. Finally, the delayed application of the protection can induce the transformation of previously formed corrosion products. For instance, sulfate green rust is integrally transformed into carbonate green rust. Other compounds, such as magnetite, are not affected. The importance of the modifications induced by cathodic protection consequently depends on the composition of the pre-existing rust layer.
Mots clés : Protection cathodique / acier au carbone / corrosion résiduelle / marnage / micro-spectroscopie Raman
Key words: Cathodic protection / carbon steel / residual corrosion / tidal zone / micro-Raman spectroscopy
© EDP Sciences, 2013
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.