Comment améliorer la durabilité de bétons plus éco-respectueux grâce à des polymères bactériens
How to improve the durability of concrete more eco-friendly using bacterial polymers
1 Nancy Université UMR 7198 IJL-CP2S-207, IUT de Nancy Brabois dpt GC, Le Montet, Rue du Doyen Urion, 54600 Villers les Nancy, France
e-mail: sebastien.roux@iutnb.uhp-nancy.fr
2 IMFS-INSA de Strasbourg, 24 boulevard de la Victoire, 67084 Strasbourg Cedex, France
e-mail: nicolas.bur@insa-strasbourg.fr; francoise.feugeas@insa-strasbourg.fr
3 UPMC, LISE, UPR 15 du CNRS, case 133, 4 place Jussieu, 75252 Paris Cedex 05, France
e-mail: bernard.tribollet@upmc.fr
Reçu : 24 Février 2011
Accepté : 11 Juillet 2011
La corrosion des armatures est une pathologie fréquente des ouvrages du génie civil pour laquelle les moyens de lutte ne sont généralement pas satisfaisants sur le plan environnemental. L’objectif de cette étude est d’évaluer un adjuvant inhibiteur de corrosion dont le principe actif est un biopolymère écorespectueux aux propriétés inhibitrices de corrosion des aciers. Des échantillons ont été réalisés à partir de deux nuances cimentaires, le traditionnel CEM I et un CEM V, plus écorespectueux car contenant des résidus et sous-produits industriels. Des essais d’imbibition capillaire et de porosité totale à l’eau ont montré la faible influence de l’adjuvant aux biopolymères sur la structure poreuse des mortiers. Après immersion en eau de mer naturelle de pâtes de ciment renforcées d’une armature en acier C15, des mesures électrochimiques ont montré que ce biopolymère n’influence pas le potentiel libre de corrosion des armatures ni la composition de leur couche passive mais inhibe la réaction cathodique de réduction de l’oxygène.
Abstract
Rebars corrosion is a common pathology of civil engineering works for which the protective and curative solutions are generally not in agreement with environmental considerations. This study aims to evaluate a corrosion inhibitor admixture whose active component is an ecofriendly biopolymer having corrosion inhibiting properties. The samples were manufactured using 2 cement bases including a CEM V that is more ecofriendly than traditional CEM I because containing industrial residues and byproducts. Capillary imbibition tests and water total porosity showed the low influence of the admixture on the pore structure of mortars. After immersion in natural seawater of cement pastes reinforced with steel C15 rebars, electrochemical measurements showed that the biopolymer does not affect the free corrosion potential of reinforcement nor the composition of passive layer but inhibits the cathodic reaction of oxygen reduction.
Mots clés : Matériaux cimentaires / biopolymères / corrosion / durabilité / porosité
Key words: Cement-based materials / biopolymers / corrosion / durability / porosity
© EDP Sciences, 2011
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.