Tenue à la fatigue des composites métalliques
Composite beams : fatigue life study of chromium electroplated motor rings
Laboratoire de physique des matériaux, Institut supérieur des matériaux et de la construction mécanique (ISMCM), Saint-Ouen.
Abstract
Fatigue tests have been carried out on chromed piston rings. Chromium is electroplated on the outer cylinder of the rings.
The presence of a brittle metal on the surface (when the martensitic ductile iron does not present initial macroscopic defects), gives the beginning of the fatigue crack on this surface. In this case initiated crack in the chromium propagates easily in the cast iron.
The tests have been carried out in air, at the ambiant temperature and at an imposed forced displacement. They are of two types :
- —
torque flexure combined tests, where the ring works as a helicoidal spring (TFC tests) ;
- —
flexure tests on prestrained ring, where we open and close the gaps of the ring (FSP tests).
© SIRPE 1989
Les statistiques affichées correspondent au cumul d'une part des vues des résumés de l'article et d'autre part des vues et téléchargements de l'article plein-texte (PDF, Full-HTML, ePub... selon les formats disponibles) sur la platefome Vision4Press.
Les statistiques sont disponibles avec un délai de 48 à 96 heures et sont mises à jour quotidiennement en semaine.
Le chargement des statistiques peut être long.