Corrosion characteristics of high-purity and Mo- or W-added Fe-Cr alloys

Caractéristiques de corrosion des alliages de haute pureté Fe-Cr : effet des additions de Mo et W

¹ Osaka Science & Technology Center, Osaka 550-0004, Japan
² Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan

Abstract

Using high purity iron-chromium alloys with 30 to 60 mass % Cr, which had been hardly produced because of embrittlement, the effects of Cr content, addition of alloying elements (Mo or W), and purification on the corrosion resistance of these alloys were investigated. From the results of electrochemical measurement and XPS analysis, it was found that general corrosion resistance is improved by addition of W or Mo and purification, and pitting corrosion resistance is improved by the increase of Cr content and the addition of Mo or W. The effect of Mo addition on pitting potential is 5 times as much as that of Cr, and the effect of W addition on pitting potential is twice as much as that of Cr. It is concluded that Fe-30 to 60 mass% Cr alloys are excellent in corrosion resistance.

Résumé

En utilisant des alliages Fe-Cr de haute pureté à 30-60 % Cr (% en masse), qui ont été rarement produits en raison de leur fragilité potentielle, on a étudié les effets de la teneur en Cr, des additions de Mo et W, et de la purification sur la résistance à la corrosion de ces alliages. A partir de mesures électrochimiques et d’analyses de surface (XPS), on a trouvé que la résistance à la corrosion générale est améliorée par l’addition de Mo ou W et par la purification, et que la résistance à la corrosion par piqûre est améliorée par l’augmentation de la teneur en Cr et l’addition de Mo ou W. L’effet d’une addition de Mo sur le potentiel de piqûre est cinq fois supérieur à celui du Cr alors que l’effet du W est deux fois celui du Cr. Il apparaît que les alliages Fe-30 à 60 % Cr (% en masse) ont une excellente résistance à la corrosion.